30CrMoV9 DIN1.7707 Nitriding Steel

30CrMoV9 DIN1.7707 Nitriding Steel 30crmov9 30CrMoV9 DIN1.7707  Nitriding Steel 30CrMoV9 DIN1

30CrMoV9 DIN1.7707 Nitriding Steel


Structural parts of medium and large cross sections and high surface hardness, e.g., valve and gate valves, cylinders for combustion engines, superheated steam valves and fittings.

All Grades Comparison

1.7707 30CrMoV9

Quality Standard

EN 10250 Open steel die forgings for general engineering purposes. Alloy special steels

Chemical Composition(%)

C Mn Si P S Cr Ni Mo V
0.26-0.34 0.40-0.70 0.40 max 0.035 max 0.035 max 2.30-2.70 0.60 max 0.15-0.25 0.10-0.20

Mechanical Properties(T=20°C if not differently stated)

Process Diameter(mm) Tensile Strength Rm (Mpa) Yield Strength Rp0.2 (Mpa) Elongation A5 (%) Impact Value Kv (J) Room Temperature
QUENCHED AND TEMPERED 160 max 900 min 700 min 12 min 35 min
QUENCHED AND TEMPERED 160-330 800 min 590 min 14 min 35 min


  • Soft Annealing: Heat to 680-720oC, cool slowly. This will produce a maximum Brinell hardness of 248.
  • Nitriding:
    Gas/plasma nitriding temperature (gas, salt bath): 570-580oC
    Gas/plasma nitriding temperature (powder, plasma): 580oC
    Surface hardness after nitriding: 800 HV
  • Hardening: Harden from a temperature of 850-880oC followed by oil quenching.
  • Tempering:Tempering temperature: 570-680oC.
  • Forging:

    Hot forming temperature: 1050-850oC.

    Mill′s test certificate:

    EN 10204/3.1 with all relevant data reg. chem. composition, mech. properties and results of testing.

    About Us

    Founded in 1998, FuShun covers an area of 3000 square meters, annual sales volume of 20000 tons. We are engaged in the import and export of Tool Steel, Iron Alloy Steel and other special steel products… More Info

    Contact Lists

    General Manager: Ms. Florence

    Sales Manager for American, Oceanian, Asian market: Mr. Crane

    Sales Manager for European, African, Asia market: Miss Summer