Spheroidizing Annealing

Spheroidizing Annealing spheroidizing annealing Spheroidizing Annealing Spheroidizing Annealing

Spheroidizing Annealing

Spheroidizing Annealing spheroidizing annealing Spheroidizing Annealing Spheroidizing Annealing

Spheroidizing Annealing

Spheroidize Annealing


Spheroidize annealing is applicable to steels which have more than 0.8% carbon. Parts are heated to between 1150°F and 1200°F and holding it at this temperature for a period of time to convert the microstructure. Essentially, cementite changes from a lamella formation to an alpha ferrite matrix with particles of spheroidal cementite (Fe3C). Spherodize annealing is generally done on parts which have been work hardened, to allow them to be further worked, either rolled in the case of coils, or drawn for wire. This resulting product has improved ductility and toughness with reduced hardness and strength. Spherodize annealing is normally carried out under a protective (endothermic) atmosphere to prevent oxidation and decarburization.

We can supply follows heat treatment services:

Normalizing, Annealing, Quenching, Tempering, Carburizing, Nitriding, High-frequency surface hardening and other processing services.

And we can strictly enforce the national standards.

And we have follows heating equipment:

  Pit furnace: Dia1300mm max, Length9500mm max.
  Salt bath furnace: Length1900mm max, Width1600mm max, Height900mm max.
  Trolley furnace: Legth15000mm max, Width6000mm max, Height6000mm max.
Tunnel type continuous reheating furnace:dia30mm-dia250mm
Induction quenching line: dia15mm-dia120mm
Normalizing cooling fan can be used in combination of wind capacity air-cooled systems.