manufacturer of tool steel, stainless steel, nickel alloy, alloy steel

1.2367 X38CrMoV5-3 Hot Work Die Steel

1.2367 X38CrMoV5-3 Hot Work Die Steels

1.2367 X38CrMoV5-3 Hot Work Die Steels

1.2367 X38CrMoV5-3 Hot Work Die Steels

1 1.2367 Properties:

1.2367 Chrome–molybdenum–vanadium steel for hardening in oil and in air with very good hardenability, high firmness during the heat and resistance to the tempering, very good toughness and plastic properties during normal and also higher temperatures. Further the steel has a very good resistance to tearing of thermal fatigue and low sensitivity to quick changes of temperature. This hot work die steel is appropriate for the heat treatment also for firmness over 1800 N/mm2 and for tools cooled by water. It is well-workable during the heat and well-workable in the soft-annealed state. At request it can also be delivered in ESR quality.

We can provide more services:

1、Hardening and tempering
2、Vacuum heat treatment
3、Polished bright surface
4、Milling bright surface
5、CNC machine
6、Deep drilling
7、Cut into small pieces
8、Make it closer to the mold
Welcome to inquiry price from drawing

2 1.2367 Applications:

Wear resisting tools, pressure die casting tools, pressing tools for light and heavy metal. For the highest requirements we recommend ESR or EFS quality.

3 Quality Standard:

BS EN ISO 4957-2000 Tool steels

4 All Grades Comparison:

ISO DIN
X38CrMoV5-3 1.2367

5 1.2367 Chemical Composition(%):

C Si Mn P S Cr Mo V
0.35-0.40 0.30-0.50 0.30-0.60 0.030 max 0.030 max 4.70-5.20 2.70-3.30 0.40-0.70

6 HEAT TREATMENT:

FORGING: Hot forming temperature: 1080-900oC.

SOFT ANNEALING: Heat to 800-840oC, cool slowly in furnace. This will produce a maximum Brinell hardness of 235.

STRESS RELIEVING: Stress relieving to remove machining stresses should be carried out by heating to 650oC, holding for one hour at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.

HARDENING: Harden from a temperature of 1030-1080oC followed by air, oil or warm bath (500-550oC) quenching. Hardness after quenching is 53-57 HRC.

TEMPERING:

Tempering Temperature (oC) Hardness (HRC) Tensile Stregth (N/mm2)
100oC 57 2140
200oC 55 1980
300oC 54 1910
400oC 53 1845
500oC 55.5 2010
550oC 56 2050
600oC 53 1845
650oC 43 1360
700oC 31 995

7 Mill′s test certificate:

EN 10204/3.1 with all relevant data reg. chem. composition, mech. properties and results of testing.

About Us

Founded in 1998, FuShun covers an area of 3000 square meters, annual sales volume of 20000 tons. We are engaged in the manufacture and export of Tool Steel, Nickel Alloy, Stainless Steel and other special steel products…,View more content About Me.

Contact Lists

General Manager: Ms. Florence

info@fushunspecialsteel.com

Get A Free Quote!

Fushun TEL: +86-731-89903933

Fushun FAX: +86-731-89853933

General Manager: Ms. Florence Tang

Whatsapp/Phone/WeChat:+86-13319591838

Find your steel grade and get a quote today.

NOW Send Your Inquiry To : info@fushunspecialsteel.com

Whatsapp:+86-18692275455

x