1.2362, X63CrMoV5–1, Cold Work Tool Steel
Product Description
Material 1.2362 (X63CrMoV5-1) is used for intermediate rolls in multi-roll stands, deburring dies and punches, cutting plates and punches, hot shears, ejection pins, drop-forging dies and hole punches.
Cutting:
Precision cutting to standard dimensions
Custom cutting according to client specifications
Cold Work Tool Steel Dimensions
We offer premium cold work tool steel in various forms, manufactured with advanced 5000-ton forging press technology for superior density and performance.
| Product Form | Specifications |
|---|---|
| Forged Round Bar | Dia. up to 1200mm |
| Forged Flat Bar | Thickness 100-600mm, Width 300-2000mm |
| Rolled Round Bar | Dia. 10-200mm |
| Hot Rolled Plate | Thickness 1-100mm, Width 60-1600mm |
Properties
Toughness & Ductility : good
Wear Resistance : good
Compressive strength : high
Dimensional stability : good
Applications
Machine knife (for producers)
Fine Blanking, Stamping, Blanking
Rolling
Cold Forming
Rolls
Material designation
1.2362 SEL
X63CrMoV5-1
Chemical composition (wt. %)
| C | Si | Mn | Cr | Mo | Ni |
| 0.63 | 1.10 | 0.40 | 5.30 | 1.20 | 0.30 |
Delivery condition
Annealed
Hardness (HB) max. 240
Annealing
Temperature 800 to 850 °C | 1,472 to 1,562 °F Slow controlled cooling in furnace at a rate of 50 to 68°F/hr (10 to 20°C/hr) down to approx. 600°C, further cooling in air.
Stress relieving
Temperature 650 °C | 1,202 °F Slow cooling in furnace; intended to relieve stresses set up by extensive machining, or in complex shapes. After through heating, hold in neutral atmosphere for 1 to 2 hours.
Hardening and Tempering
Temperature 980 to 1,020 °C | 1,796 to 1,868 °F Oil, salt bath from 842 to 932°F (450 to 500°C), air (small sizes only) Holding time after temperature equalization: 15 to 30 minutes. Obtainable hardness: approx. 62 HRc