1.2601 X165CrMoV12 Cold Work Tool Steel
1.2601 X165CrMoV12 Cold Work Tool Steel
X165CrMoV12 1.2601 is a German Cold work tool alloy steel material grade.it is shock resisting steel. it belong to DIN 17350 standard. Digital Grade material number 1.2601. Metal Steel Grade W-Nr X165CrMoV12 It is a die steel, use in extrusion moulds, Hot Cast moulds. like aluminium production, Aluminium cutting mold.
We can provide more services:
1、Hardening and tempering
2、Vacuum heat treatment
3、Polished bright surface
4、Milling bright surface
5、CNC machine
6、Deep drilling
7、Cut into small pieces
8、Make it closer to the mold
Welcome to inquiry price from drawing
Cutting:
Precision cutting to standard dimensions
Custom cutting according to client specifications
Cold Work Tool Steel Dimensions
We offer premium cold work tool steel in various forms, manufactured with advanced 5000-ton forging press technology for superior density and performance.
| Product Form | Specifications |
|---|---|
| Forged Round Bar | Dia. up to 1200mm |
| Forged Flat Bar | Thickness 100-600mm, Width 300-2000mm |
| Rolled Round Bar | Dia. 10-200mm |
| Hot Rolled Plate | Thickness 1-100mm, Width 60-1600mm |
Applications
Cutting tools, stamping, woodworking, drawing, deep drawing and pressing tools, cold working
rolls , measuring tools .
Material equivalent of DIN X165CrMoV12 | 1.2601 steel
| Germany | Italy | Sweden | Spain |
| DIN,WNr | UNI | SS | UNE |
| X165CrMoV12 | 1.2601 | X165CRMOW12KU | 2310 | X160CRMOV12 |
Chemical composition (wt.%) of 1.2601
| C | Si ≤ |
Mn ≤ |
P ≤ |
S ≤ |
Cr | Mo | Other |
| 1.55-1.75 | 0.25-0.40 | 0.20-0.40 | 0.030 | 0.030 | 11.0-12.0 | 0.50-0.70 | V 0.10-0.50 W 0.40-0.60 |
Smelting Option
1 EAF: Electric Arc Furnace
2 EAF+LF+VD: Refined-smelting and vacuum degassing
3 EAF+ESR: Electro Slag Remelting
4 EAF+PESR: protective atmosphere Electro Slag Remelting
5 VIM+PESR: Vacuum induction melting
Forming Option
1 Hot rolling process
2 Hot Forging: Electro-hydraulic; High-speed-hydraulic; Oil-hydraulic; Precision-forging
Heat-treatment Option
1 +A: Annealed (full/soft/spheroidizing)
2 +N: Normalized
3 +NT: Normalized and tempered
4 +QT: Quenched and tempered (water/oil)
Suface Option
1 Black Surface
2 Grounded: Bright but rough ; Not precision
3 Machining for plate: Bright and precision; Little turning scar
4 Peeled/Turned: Bright and precision; Little turning scar
5 Polished: Very Bright and precision size; Not turning scar
Other Services
1 Cutting: Small pieces
2 CNC Machine: Produce as your drawing
3 Package: Bare/Nylon/Canvas/Wooden
4 Payment:T/T, L/C, O/A(request credit)
5 Transport:FOB/CFR/CIF/DDU/DDP (train/ship/Air)
Mechanical Properties of 1.2601
| Rp0.2 (MPa) | Rm (MPa) | Impact KV (J) |
Elongation A (%) |
A Z (%) | Delivery | Hardness HB |
| 641 (≥) | 662 (≥) | 23 | 14 | 31 | Solution & Aging, Ann, Ausaging, Q+T | 142 |
Heat treatment of X165CrMoV12 | 1.2601 Cold work tool steel
Annealing: Annealing temperature/℃: 800~830; After the annealing, degree of hardness ≤HBS: 255
Quenching: Hardening temperature/℃: 980~1010, Quenching in oil or air
Tempering: Commonly used drawing temperature/℃: 180~250; After tempering hardness HRC | 100 ℃ : 63; After tempering hardness HRC | 200 ℃ : 61; After tempering hardness HRC | 300 ℃ : 60 ; After tempering hardness HRC | 400 ℃ : 58
Normalizing：at Normalizing temperature, then cool in furnace